EN 10025 Steel Properties
The below table outlines the material properties for EN 10025 material including the young's modulus, yield strength, ultimate strength and other relevant mechanical properties required for structural and mechanical design.
-
Grade S185
-
Grade S235JR, S235JRG1
-
Grade S235JRG2
-
Grade S235J0
-
Grade S235J2G3, S235J2G4
-
Grade S275JR, S275J0, S275J2G3, S275J2G4
-
Grade S350J0
-
Grade S355JR, S355J0, S355J2G3, S355J2G4, S355K2G3, S355K2G4
-
Grade S420
-
Grade S690QL
-
Grade S890Q
-
Grade E295
-
Grade E335
-
Grade E360
EN 10025 Young's Modulus
The Young's Modulus of EN 10025 is 210,000 MPa.
EN 10025 Ultimate Strength
The Ultimate Strength of EN 10025 ranges between 380 and 1,020 MPa.
EN 10025 Yield Strength
The Yield Strength of EN 10025 ranges between 155 and 890 MPa depending on the material grade. See the below tables to get your specific material grade material strength.
Grade S185 Steel Properties
Thickness < 3mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 425 MPa | 185 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 62 ksi | 27 ksi | 6.67 1/°F | 0.3 |
3mm ≤ Thickness ≤ 16mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 400 MPa | 185 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 58 ksi | 27 ksi | 6.67 1/°F | 0.3 |
16mm < Thickness ≤ 40mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 400 MPa | 175 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 58 ksi | 25 ksi | 6.67 1/°F | 0.3 |
40mm < Thickness ≤ 100mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 400 MPa | 175 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 58 ksi | 25 ksi | 6.67 1/°F | 0.3 |
100mm < Thickness ≤ 150mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 390 MPa | 165 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 57 ksi | 24 ksi | 6.67 1/°F | 0.3 |
150mm < Thickness ≤ 200mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 380 MPa | 155 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 55 ksi | 22 ksi | 6.67 1/°F | 0.3 |
Grade S235JR, S235JRG1 Steel Properties
Thickness < 3mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 435 MPa | 235 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 63 ksi | 34 ksi | 6.67 1/°F | 0.3 |
3mm ≤ Thickness ≤ 16mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 235 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 34 ksi | 6.67 1/°F | 0.3 |
16mm < Thickness ≤ 40mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 225 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 33 ksi | 6.67 1/°F | 0.3 |
40mm < Thickness ≤ 100mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 215 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 31 ksi | 6.67 1/°F | 0.3 |
100mm < Thickness ≤ 150mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 425 MPa | 195 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 62 ksi | 28 ksi | 6.67 1/°F | 0.3 |
150mm < Thickness ≤ 200mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 415 MPa | 185 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 60 ksi | 27 ksi | 6.67 1/°F | 0.3 |
200mm < Thickness ≤ 250mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 415 MPa | 175 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 60 ksi | 25 ksi | 6.67 1/°F | 0.3 |
Grade S235JRG2 Steel Properties
Thickness < 3mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 435 MPa | 235 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 63 ksi | 34 ksi | 6.67 1/°F | 0.3 |
3mm ≤ Thickness ≤ 16mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 235 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 34 ksi | 6.67 1/°F | 0.3 |
16mm < Thickness ≤ 40mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 225 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 33 ksi | 6.67 1/°F | 0.3 |
40mm < Thickness ≤ 63mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 215 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 31 ksi | 6.67 1/°F | 0.3 |
63mm < Thickness ≤ 80mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 215 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 31 ksi | 6.67 1/°F | 0.3 |
80mm < Thickness ≤ 100mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 215 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 31 ksi | 6.67 1/°F | 0.3 |
100mm < Thickness ≤ 150mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 195 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 28 ksi | 6.67 1/°F | 0.3 |
150mm < Thickness ≤ 200mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 395 MPa | 185 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 57 ksi | 27 ksi | 6.67 1/°F | 0.3 |
200mm < Thickness ≤ 250mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 395 MPa | 175 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 57 ksi | 25 ksi | 6.67 1/°F | 0.3 |
Grade S235J0 Steel Properties
Thickness < 3mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 435 MPa | 235 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 63 ksi | 34 ksi | 6.67 1/°F | 0.3 |
3mm ≤ Thickness ≤ 16mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 235 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 34 ksi | 6.67 1/°F | 0.3 |
16mm < Thickness ≤ 40mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 225 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 33 ksi | 6.67 1/°F | 0.3 |
40mm < Thickness ≤ 63mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 215 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 31 ksi | 6.67 1/°F | 0.3 |
63mm < Thickness ≤ 80mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 215 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 31 ksi | 6.67 1/°F | 0.3 |
80mm < Thickness ≤ 100mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 215 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 31 ksi | 6.67 1/°F | 0.3 |
100mm < Thickness ≤ 150mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 195 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 28 ksi | 6.67 1/°F | 0.3 |
150mm < Thickness ≤ 200mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 395 MPa | 185 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 57 ksi | 27 ksi | 6.67 1/°F | 0.3 |
200mm < Thickness ≤ 250mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 395 MPa | 175 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 57 ksi | 25 ksi | 6.67 1/°F | 0.3 |
Grade S235J2G3, S235J2G4 Steel Properties
Thickness < 3mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 435 MPa | 235 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 63 ksi | 34 ksi | 6.67 1/°F | 0.3 |
3mm ≤ Thickness ≤ 16mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 235 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 34 ksi | 6.67 1/°F | 0.3 |
16mm < Thickness ≤ 40mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 225 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 33 ksi | 6.67 1/°F | 0.3 |
40mm < Thickness ≤ 63mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 215 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 31 ksi | 6.67 1/°F | 0.3 |
63mm < Thickness ≤ 80mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 215 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 31 ksi | 6.67 1/°F | 0.3 |
80mm < Thickness ≤ 100mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 215 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 31 ksi | 6.67 1/°F | 0.3 |
100mm < Thickness ≤ 150mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 405 MPa | 195 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 59 ksi | 28 ksi | 6.67 1/°F | 0.3 |
150mm < Thickness ≤ 200mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 395 MPa | 185 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 57 ksi | 27 ksi | 6.67 1/°F | 0.3 |
200mm < Thickness ≤ 250mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 395 MPa | 175 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 57 ksi | 25 ksi | 6.67 1/°F | 0.3 |
Grade S275JR, S275J0, S275J2G3, S275J2G4 Steel Properties
Thickness < 3mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 505 MPa | 275 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 73 ksi | 40 ksi | 6.67 1/°F | 0.3 |
3mm ≤ Thickness ≤ 16mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 485 MPa | 275 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 70 ksi | 40 ksi | 6.67 1/°F | 0.3 |
16mm < Thickness ≤ 40mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 485 MPa | 265 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 70 ksi | 38 ksi | 6.67 1/°F | 0.3 |
40mm < Thickness ≤ 63mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 485 MPa | 255 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 70 ksi | 37 ksi | 6.67 1/°F | 0.3 |
63mm < Thickness ≤ 80mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 485 MPa | 245 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 70 ksi | 36 ksi | 6.67 1/°F | 0.3 |
80mm < Thickness ≤ 100mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 485 MPa | 235 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 70 ksi | 34 ksi | 6.67 1/°F | 0.3 |
100mm < Thickness ≤ 150mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 470 MPa | 225 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 68 ksi | 33 ksi | 6.67 1/°F | 0.3 |
150mm < Thickness ≤ 200mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 460 MPa | 215 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 67 ksi | 31 ksi | 6.67 1/°F | 0.3 |
200mm < Thickness ≤ 250mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 505 MPa | 205 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 73 ksi | 30 ksi | 6.67 1/°F | 0.3 |
Grade S350J0 Steel Properties
Thickness < 16mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 635 MPa | 450 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 92 ksi | 65 ksi | 6.67 1/°F | 0.3 |
16mm < Thickness ≤ 40mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 635 MPa | 430 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 92 ksi | 62 ksi | 6.67 1/°F | 0.3 |
40mm < Thickness ≤ 63mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 635 MPa | 410 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 92 ksi | 59 ksi | 6.67 1/°F | 0.3 |
63mm < Thickness ≤ 80mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 635 MPa | 390 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 92 ksi | 57 ksi | 6.67 1/°F | 0.3 |
80mm < Thickness ≤ 100mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 635 MPa | 380 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 92 ksi | 55 ksi | 6.67 1/°F | 0.3 |
100mm < Thickness ≤ 150mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 615 MPa | 380 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 89 ksi | 55 ksi | 6.67 1/°F | 0.3 |
Grade S355JR, S355J0, S355J2G3, S355J2G4, S355K2G3, S355K2G4 Steel Properties
Thickness < 3mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 595 MPa | 355 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 86 ksi | 51 ksi | 6.67 1/°F | 0.3 |
3mm ≤ Thickness ≤ 16mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 560 MPa | 355 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 81 ksi | 51 ksi | 6.67 1/°F | 0.3 |
16mm < Thickness ≤ 40mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 560 MPa | 345 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 81 ksi | 50 ksi | 6.67 1/°F | 0.3 |
40mm < Thickness ≤ 63mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 560 MPa | 335 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 81 ksi | 49 ksi | 6.67 1/°F | 0.3 |
63mm < Thickness ≤ 80mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 560 MPa | 325 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 81 ksi | 47 ksi | 6.67 1/°F | 0.3 |
80mm < Thickness ≤ 100mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 560 MPa | 315 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 81 ksi | 46 ksi | 6.67 1/°F | 0.3 |
100mm < Thickness ≤ 150mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 550 MPa | 295 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 80 ksi | 43 ksi | 6.67 1/°F | 0.3 |
150mm < Thickness ≤ 200mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 540 MPa | 285 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 78 ksi | 41 ksi | 6.67 1/°F | 0.3 |
200mm < Thickness ≤ 250mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 540 MPa | 275 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 78 ksi | 40 ksi | 6.67 1/°F | 0.3 |
Grade S420 Steel Properties
Thickness ≤ 16mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 600 MPa | 420 MPa | 12 1/°C | 0.3 |
| Imperial | 200,000 ksi | 7,850 lb/ft3 | 87 ksi | 61 ksi | 12 1/°F | 0.3 |
16mm < Thickness ≤ 40mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 600 MPa | 400 MPa | 12 1/°C | 0.3 |
| Imperial | 200,000 ksi | 7,850 lb/ft3 | 87 ksi | 58 ksi | 12 1/°F | 0.3 |
40mm < Thickness ≤ 63mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 600 MPa | 390 MPa | 12 1/°C | 0.3 |
| Imperial | 200,000 ksi | 7,850 lb/ft3 | 87 ksi | 57 ksi | 12 1/°F | 0.3 |
63mm < Thickness ≤ 80mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 600 MPa | 370 MPa | 12 1/°C | 0.3 |
| Imperial | 200,000 ksi | 7,850 lb/ft3 | 87 ksi | 54 ksi | 12 1/°F | 0.3 |
80mm < Thickness ≤ 100mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 600 MPa | 360 MPa | 12 1/°C | 0.3 |
| Imperial | 200,000 ksi | 7,850 lb/ft3 | 87 ksi | 52 ksi | 12 1/°F | 0.3 |
100mm < Thickness ≤ 150mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 575 MPa | 340 MPa | 12 1/°C | 0.3 |
| Imperial | 200,000 ksi | 7,850 lb/ft3 | 83 ksi | 49 ksi | 12 1/°F | 0.3 |
150mm < Thickness ≤ 200mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 575 MPa | 330 MPa | 12 1/°C | 0.3 |
| Imperial | 200,000 ksi | 7,850 lb/ft3 | 83 ksi | 48 ksi | 12 1/°F | 0.3 |
200mm < Thickness ≤ 250mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 575 MPa | 320 MPa | 12 1/°C | 0.3 |
| Imperial | 200,000 ksi | 7,850 lb/ft3 | 83 ksi | 46 ksi | 12 1/°F | 0.3 |
Grade S690QL Steel Properties
3mm < Thickness ≤ 50mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 855 MPa | 690 MPa | 12 1/°C | 0.3 |
| Imperial | 200,000 ksi | 7,850 lb/ft3 | 124 ksi | 100 ksi | 12 1/°F | 0.3 |
50mm < Thickness ≤ 100mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 845 MPa | 650 MPa | 12 1/°C | 0.3 |
| Imperial | 200,000 ksi | 7,850 lb/ft3 | 123 ksi | 94 ksi | 12 1/°F | 0.3 |
100mm < Thickness ≤ 150mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 805 MPa | 630 MPa | 12 1/°C | 0.3 |
| Imperial | 200,000 ksi | 7,850 lb/ft3 | 117 ksi | 91 ksi | 12 1/°F | 0.3 |
Grade S890Q Steel Properties
12mm ≤ Thickness ≤ 50mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 1,020 MPa | 890 MPa | 12 1/°C | 0.3 |
| Imperial | 200,000 ksi | 7,850 lb/ft3 | 148 ksi | 129 ksi | 12 1/°F | 0.3 |
Grade E295 Steel Properties
Thickness < 3mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 575 MPa | 295 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 83 ksi | 43 ksi | 6.67 1/°F | 0.3 |
3mm ≤ Thickness ≤ 16mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 540 MPa | 295 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 78 ksi | 43 ksi | 6.67 1/°F | 0.3 |
16mm < Thickness ≤ 40mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 540 MPa | 285 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 78 ksi | 41 ksi | 6.67 1/°F | 0.3 |
40mm < Thickness ≤ 63mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 540 MPa | 275 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 78 ksi | 40 ksi | 6.67 1/°F | 0.3 |
63mm < Thickness ≤ 80mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 540 MPa | 265 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 78 ksi | 38 ksi | 6.67 1/°F | 0.3 |
80mm < Thickness ≤ 100mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 540 MPa | 255 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 78 ksi | 37 ksi | 6.67 1/°F | 0.3 |
100mm < Thickness ≤ 150mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 530 MPa | 245 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 77 ksi | 36 ksi | 6.67 1/°F | 0.3 |
150mm < Thickness ≤ 200mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 525 MPa | 235 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 76 ksi | 34 ksi | 6.67 1/°F | 0.3 |
200mm < Thickness ≤ 250mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 525 MPa | 225 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 76 ksi | 33 ksi | 6.67 1/°F | 0.3 |
Grade E335 Steel Properties
Thickness < 16mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 680 MPa | 335 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 99 ksi | 49 ksi | 6.67 1/°F | 0.3 |
16mm < Thickness ≤ 40mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 640 MPa | 325 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 93 ksi | 47 ksi | 6.67 1/°F | 0.3 |
40mm < Thickness ≤ 63mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 640 MPa | 315 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 93 ksi | 46 ksi | 6.67 1/°F | 0.3 |
63mm < Thickness ≤ 80mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 640 MPa | 305 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 93 ksi | 44 ksi | 6.67 1/°F | 0.3 |
80mm < Thickness ≤ 100mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 640 MPa | 295 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 93 ksi | 43 ksi | 6.67 1/°F | 0.3 |
100mm < Thickness ≤ 150mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 630 MPa | 275 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 91 ksi | 40 ksi | 6.67 1/°F | 0.3 |
150mm < Thickness ≤ 200mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 625 MPa | 265 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 91 ksi | 38 ksi | 6.67 1/°F | 0.3 |
Grade E360 Steel Properties
Thickness < 3mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 795 MPa | 360 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 115 ksi | 52 ksi | 6.67 1/°F | 0.3 |
3mm ≤ Thickness ≤ 16mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 750 MPa | 360 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 109 ksi | 52 ksi | 6.67 1/°F | 0.3 |
16mm < Thickness ≤ 40mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 750 MPa | 355 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 109 ksi | 51 ksi | 6.67 1/°F | 0.3 |
40mm < Thickness ≤ 63mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 750 MPa | 345 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 109 ksi | 50 ksi | 6.67 1/°F | 0.3 |
63mm < Thickness ≤ 80mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 750 MPa | 335 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 109 ksi | 49 ksi | 6.67 1/°F | 0.3 |
80mm < Thickness ≤ 100mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 750 MPa | 325 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 109 ksi | 47 ksi | 6.67 1/°F | 0.3 |
100mm < Thickness ≤ 150mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 740 MPa | 305 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 107 ksi | 44 ksi | 6.67 1/°F | 0.3 |
150mm < Thickness ≤ 200mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 735 MPa | 295 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 107 ksi | 43 ksi | 6.67 1/°F | 0.3 |
200mm < Thickness ≤ 250mm Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 210,000 MPa | 7,850 kg/m3 | 735 MPa | 285 MPa | 12 1/°C | 0.3 |
| Imperial | 30,458 ksi | 491 lb/ft3 | 107 ksi | 41 ksi | 6.67 1/°F | 0.3 |